Hot melt double-sided adhesive tape (including release paper) is a hot melt adhesive film made by extrusion casting or scraping process, and the subsequent process is to be cut by a slitting machine and rolled into a disc. At room temperature, it appears solid and non viscous; When the temperature rises during lamination, it will melt, and both sides will have viscosity, making it an environmentally friendly adhesive. Due to its structure resembling a thin film, with the entire surface covered in adhesive, the bonding strength far exceeds that of hot melt adhesive film. The main component of this rubber strip is TPU, which is polyurethane. Hot melt double-sided adhesive tape made from TPU has excellent adhesion to various materials such as textile fabrics, leather, TPU films, sponges, etc. It also has good water resistance and softness, and is widely used in clothing, home building materials, shoe materials, clothing and apparel, and other fields. There are roughly two types of hot-melt double-sided adhesive tapes: one with high elasticity and the other with ordinary low elasticity. The high elasticity tape has outstanding elasticity and good rebound, suitable for seamless underwear and fields that require high elasticity. It has a high melting point, excellent high temperature resistance, high transparency, but also relatively high cost; Ordinary adhesive tape has average elasticity, lower tensile strength and resilience than high elasticity tape, and lower operating temperature and cost compared to high elasticity tape. It is commonly used in ordinary clothing and other industrial applications, with transparent or thin film colors.

We have our own factory and produce independently. The thinnest thickness we can produce is 0.01mm, and the highest thickness is 0.5mm. The narrowest width of the cutting disc and strip can cut 0.5cm adhesive film strips. We can customize high-purity adhesive films for you, as well as adhesive films with three types of peeling substrates: red film, transparent film, release paper, etc. We offer three different types of hot melt adhesive films, with uniform density, water resistance, yellowing resistance, and strong adhesion. The tablet laminating machine is easy to operate and can effectively reduce the waste of substrate materials, reducing costs and saving labor for enterprises!

Product type:☑G0117p  ☑G0217p  ☑G6016p ☑G0216p ☑GPP8802   ☑Gev0808

Elastic stretch TPU hot melt adhesive film

Applicable adhesive materials: ✔ Textile fabrics ✔ Polyurethane sponge foam ✔ Paper ✔ rubber ✔ TPU laminated film ✔ genuine leather ✔ metal

Applicable fields: ✔ Clothing and daily necessities ✔ Shoe material field ✔ Luggage industry ✔ Home textile interior ✔ Automotive Interior ✔ Medical Products ✔ lamination

characteristic:

◈ Good breathability ◈ Good adhesion to textiles, leather, sponges, and TPU film materials

◈ Excellent washability, can be cleaned multiple times without opening the glue ◈ Transparent color, elastic and stretchable

Elastic stretch TPU hot melt adhesive film

Applicable adhesive materials: ✔ Textile fabrics ✔ genuine leather ✔ TPU FILM ✔ Polyurethane sponge foam ✔ Paper rubber ✔ PVC leather wooden board ✔ metal

Applicable fields: ✔ daily necessities ✔ Architectural decoration ✔ Medical Products ✔ Shoe material field ✔ Automotive Interior ✔ clothing

characteristic:

◈ Good breathability ◈ Good washability ◈ Semi transparent matte color, no elasticity

Has good adhesion to leather, sponge, wood products, and textiles

Technical data:

*******************************************************************

Reference Usgae:

Hot melt adhesive requires hot pressing bonding.

1. Stick two types of substrate materials together, stack (Material 1)/(Hot Melt Adhesive Film)/(Material 2) together, and use a hot melt adhesive bonding machine or a professional flat hot melt adhesive laminating machine or iron for hot press bonding. The reference temperature is 15-25 degrees higher than the melting point of the substrate. For example, if the melting point of the mesh adhesive film is 110 degrees, the machine will set the hot pressing temperature to around 130 degrees and the pressure to 0.2-0.5 Mpa for 5-10 seconds. The specific laminating conditions need to be adjusted according to the actual situation of the customer. When bonding thick metal substrates, lay the adhesive (hot melt adhesive film or film) on the thick metal substrate and bake or heat press it together in an oven at 145 ℃ -165 ℃. After the adhesive film is completely melted, the two materials can be bonded together, and the baking temperature can be adjusted according to the actual situation of the customer.

2. Thinner metal materials can also be pressed using a hot stamping press, such as thin aluminum plates, thin copper plates, thin steel plates, etc., and bonded to non-woven fabrics.

Transportation and storage:

Hot melt adhesive film and hot melt adhesive mesh should be handled carefully during transportation. Try to avoid sunlight, rain, high temperature, and high pressure as much as possible. During the loading process, it is prohibited to use heavy tools such as iron hooks for lifting.

Please ensure that the packaging is intact during unloading. The goods can be stored in a cool, ventilated, dry place with a temperature of 0-30 ℃ (humidity ≤ 70% RH), away from high temperatures, and the stacking height should not exceed 3 layers.

Shelf life: 12-36 months from the date of production.